Jun 13, 2023
Metagenomic insights into nutrient and hypoxic microbial communities at the macrofouling/steel interface leading to severe MIC
npj Materials Degradation
npj Materials Degradation volume 7, Article number: 41 (2023) Cite this article
187 Accesses
Metrics details
Adherent macrofouling in marine environments caused complex corrosion of steel surfaces, resulting in localized corrosion at the oyster/steel interface and uniform corrosion at the ascidian/steel interface. Sulfate-reducing bacteria (SRB) have been implicated in the microbiologically influenced corrosion (MIC) process at macrofouling-covered interfaces. To better understand the role of marine biofilms as key mediators in the MIC process, metagenomic techniques were used to study microbial communities and their response to macrofouling's coverage. Compared to ascidians, the formed local anaerobic zone at oyster/steel interface stimulated the growth of SRBs, leading to higher FeS content and severe localized corrosion. SRB Desulfovibrio and Desulfobulbus, along with the SRB-related functional gene dsr, were found to increase, while oxygen-related function genes coxC, ccoN, ccoO, ccoP, and ccoQ decreased. In contrast, steel surfaces without macrofouling coverage had the richest microbial communities, yet experienced less severe MIC, suggesting no direct connection between microbial abundance/diversity and steel corrosion promotion.
Marine fouling organisms refer to the general term for animals, plants, and microorganisms attached to the surface of marine facilities. Based on body size, they are classified into microfouling organisms (micron-scale) and macrofouling organisms (centimeter-scale)1,2,3. Fouling organisms can adversely affect marine infrastructures such as ships, bridges, oil platforms, and pipelines3,4,5,6. Currently, there are two main research directions regarding the relationship between biofouling and metal marine corrosion.
First, study the effect of microorganisms on metal marine corrosion. Microorganisms are believed to contribute significantly to the process of metal rusting. Biofilm-forming microorganisms can quickly colonize metal surfaces to form a highly complex, dynamic three-dimensional (3D) structure that can accelerate or inhibit MIC7,8. Currently, research on marine corrosive microorganisms mainly focuses on culturable bacteria in the laboratory to study the effects of mixed or single colonies on metal corrosion under simulated field environments or controlled experimental conditions9,10,11. A considerable number of articles have investigated the effects of sulfate-reducing bacteria (SRB)12,13,14,15, nitrate-reducing bacteria (NRB)16,17,18, acid-producing bacteria (APB)19, and iron bacteria (IB)20,21 on metal corrosion in the marine environment. Under anoxic conditions, SRB are commonly considered the main culprits of MIC14, which can use sulfate as a terminal electron acceptor to degrade organic compounds, leading to the production of corrosive sulfides12,13,14,15. Gu et al.22,23 classified anaerobic MIC attacks into two different types: extracellular electron transfer MIC (EET-MIC) caused by the respiration of microbes, and metabolite MIC (M-MIC) caused by the secretion of corrosive metabolites. Recently, research on the mechanism of MIC has become increasingly in-depth. Zhou et al.24 found Shewanella oneidensis MR-1, an attractive model microbe, can directly consume electrons from iron-containing metals under aerobic conditions. The findings demonstrate that corrosion can occur through a significant pathway of direct electron transfer between metal and microbe. Anaerobic corrosion via flavins or H2 as electron shuttles as well as direct electron uptake from Fe0 have all been proposed as potential mechanisms for corrosion by S. oneidensis and related species25,26,27,28. Tang et al.28 found that stainless steel corrosion via direct iron-to-microbe electron transfer by Geobacter sulfurreducens and Geobacter metallireducens, which are electrotrophs that are known to directly accept electrons from other microbes or electrodes. Another representative marine electro-active bacterium, Pseudomonas aeruginosa, a pervasive bacterium competent for developing biofilms in marine habitats has been confirmed to cause severe MIC on carbon steel through extracellular electron transfer (EET)29,30,31. Zhou et al.31 found that the biocorrosion of stainless steel in marine water was accelerated via extracellular electron transfer encoding gene phzH of Pseudomonas aeruginosa. However, since there are 105–106 species of microorganisms in the environment, studying a single microorganism is limiting. Therefore, analyzing microbial communities in the corrosive marine environment also makes a significant contribution to research on marine MIC32,33. High-throughput sequencing technology provides a good idea. High-throughput sequencing, which differs from traditional Sanger (dideoxy) sequencing, is a technique that can parallel sequence a large number of nucleic acid molecules at once34,35,36,37,38. Typically, a single sequencing reaction can produce sequencing data of no less than 100 Mb. Procopio et al.38 proposed that when combined with sequencing data from environmental samples, methodologies such as metagenomics, metatranscriptome, and metabolomics will open up another horizons in understanding of the role of corrosive microbial biofilms. The emergence of high-throughput DNA sequencing techniques has facilitated the identification of microbial species that are involved in corrosion processes of alloys, both directly and indirectly38. Huttunen-Saarivirta et al.35 revealed dissimilarities between the stainless steel grades in corrosion behavior and biofouling tendency in brackish seawater using high-throughput sequencing (HTP sequencing). Zhang et al.32 utilized high-throughput sequencing to investigate the microbial community in the rust layer on the metal surface after 30 months of immersion in seawater. They proposed that each metal alloy, including carbon steel, copper alloy, and aluminum alloy, would lead to the development of a distinct microbial community. In addition, different corrosion-related microbial communities formed in the inner, middle, and outer rust layers of carbon steel.
Second, study the effect of marine macrofouling organisms on metal corrosion. Macrofouling can be categorized as soft-fouling (non-calcareous algae, sponges, and ascidians, et al.) and hard-fouling (barnacles, oysters, et al.), based on the presence or absence of calcareous shells3,39. It has been observed that the attachment of macrofouling can significantly damage the integrity and performance of offshore structures6,40,41. For instance, the macrofouling of calcareous shells, such as oysters and barnacles, can lead to severe localized corrosion of marine facilities40. The most common explanation for this phenomenon is that the adhesion of macrofouling creates a "biological confinement layer" on the steel surface. The interior of the layer becomes an oxygen-deficient environment, while there is sufficient oxygen outside the layer. The formation of oxygen concentration cells accelerates crevice corrosion at the interface between the macrofouling and steel3.
However, the interface between macrofouling and steel forms an independent ecosystem. The main components of macrofouling secretions are proteins and polysaccharides, which create a eutrophic environment that promotes microbial growth42,43,44,45. Perme et al.46 found that severe localized corrosion of underwater steel bridge piles in Florida was related to corrosion influenced by macrofouling and microorganisms. They also found that cracks formed by macrofouling pollutants have a significant impact on the growth of SRB and the development of MIC. The MIC process dominated by SRB develops rapidly in enclosed environments occupied by macrofouling organisms5. Therefore, to study the corrosion affected by macrofouling coverage, it is necessary to establish the steel corrosion mechanism under the synergistic effect of microbial community and macrofouling, by examining the interface corrosion behavior and the abundance and diversity of microorganisms.
In this study, we investigated the corrosion behavior of high-strength low-alloy steel surfaces covered by oysters (representative of hard-fouling organisms) and ascidians (representative of soft-fouling organisms) using field immersion experiments and laboratory characterization. We used high-throughput sequencing technology to study the microbial community characteristics of the rust layer at the macrofouling/steel interface, based on the corrosion types and rust layer composition. In addition, we examined the microbial communities in oyster secretions and tissues due to their role in localized corrosion. Our results showed that the heterogeneous aerobic/anaerobic microenvironment formed at the interface and the nutrient source provided by macrofouling secretions lead to the growth of anaerobic bacteria and accelerate steel corrosion. This study provides insights into the synergistic effect of macrofouling and microorganisms on steel corrosion and contributes to the study of the close relationship between microbial growth and macrofouling.
Soft-fouling and hard-fouling organisms all could pose potential threats to marine facilities. Oysters, as representatives of hard-fouling organisms, are composed of a soft body protected by two complex shell sections. The oyster shell is primarily made of 97% calcium carbonate, which provides it with significant flexural strength and low conductivity. Ascidians, on the other hand, are representatives of soft-fouling organisms. They are highly adaptable to the environment and have strong spatial competitiveness, which allows them to quickly occupy steel surfaces and alter the diversity and structural characteristics of the original benthic community.
To investigate the corrosion behavior of steel covered by soft-fouling and hard-fouling, the steel specimens were immersed in seawater for 9 months. Then, the covered macrofouling were removed after the fouled steel specimens were collected. Different corrosion types were observed between the oyster and ascidian-covered interfaces (Fig. 1). Severe localized corrosion was observed in areas where the oysters could not fully cover due to the irregular shape of their shells, while uniform corrosion was observed on the fouled steel surface covered by ascidians.
Macroscopic morphology analysis of the steel surface for specimens OY, AS, and SW after nine months of immersion. The SEM images corresponded to the interfacial rust morphology after removing the macrofouling, and the laser confocal spectroscopy corresponded to the whole bare steel surface morphology after removing the macrofouling and rust. OY, the steel surface covered by oysters; AS, the steel surface covered by ascidians; SW, the steel surface which not covered by macrofouling.
Evidence was obtained by the SEM images and the corresponding laser confocal spectroscopy (Fig. 1). Upon removing the macrofouling, it was observed from the SEM images that for steel specimen covered by oyster (OY), a large area of peeling occurred on the outer rust layer and local damage with irregular corrosion pits were generated on this area. For steel specimen which covered by ascidians (AS), the rust layer was also dense, but a flocculent structure appeared on the upper layer of the rust. For steel specimen which not covered by macrofouling (SW), the outer rust layer was loose and easily fell off, the typical morphology of steel immersed in seawater after long-term immersion47. It was not difficult to find that the secretion of the macrofouling penetrated into the rust layer and changed the structure of the rust layer, the coverage of the macrofouling changed the state of the outer rust layer.
Consistently, the CLSM results showed that after removing the rust layer, the OY specimen had a significantly destroyed steel surface, with significant local damage and corrosion gaps, while the AS specimen had a relatively uniform steel surface without obvious local damage. Maximum differences in corrosion depth values were extracted, and the maximum corrosion depth value for the OY specimen was 721.0 μm, far greater than the values of AS (453.048 μm) and SW (521.1 μm) specimens. The average roughness values were also analyzed, which the Sa average values of the bare steel surface sorted from largest to smallest were: OY > AS > SW. It was believed that macrofouling coverage affected the steel surface's roughness and promoted the initiation of corrosion pits. However, the gap formed by the covering environment of the oyster's calcareous shell further developed these corrosion pits, leading to severe localized damage and corrosion. In contrast, the corrosion pits promoted by ascidians coverage appeared to be connected in sheets, showing uniform corrosion.
The corrosion products play an important role in explaining the corrosion evolution. XPS was used to detect the elemental constituent of the rust layer formed at the macrofouling/steel interface (Fig. 2). The XPS survey scan of the corrosion products revealed that the main elements were Fe, C, O, and S. The Fe 2p high-resolution spectra (Fig. 2a) of the three specimens were decomposed to peaks at 720.148, 711.849, 725.349,50, 710.751, and 723.552 eV, related to Fe0, FeOOH 2p3/2, FeOOH 2p1/2, Fe3O4 2p3/2, and Fe3O4 2p3/2, respectively. While a peak at 713.6 eV (FeS 2p3/2)50 were found from OY-RU and AS-RU specimens, indicating that FeS was produced at macrofouling/steel interface. This conclusion could also be confirmed by S 2p high-resolution spectra (Fig. 2d). The S 2p spectra recorded from the three specimens were composed of a common peak at 169.6 eV53 corresponding to SO42− of GR(SO42−). While corrosion products of OY-RU and AS-RU specimens were decomposed to peaks at 161.0 (S2− 2p3/2) and 163.0 eV (S2− 2p1/2)54, related to FeS. The O 1s high-resolution spectra (Fig. 2c) were decomposed to peaks at 530.0 and 531.6 eV, related to OH− and O2−, respectively55. The C 1s high-resolution spectra (Fig. 2e) revealed three peaks: carboxylate groups (O=C–O) at 289.1 eV, C–C bond at 284.6 eV, and C–O bond at 286.1 eV. The C–C may result from aliphatic carbon, and C–C result from carbon single bonded to oxygen from polysaccharides or peptides/proteins56,57. The carboxylate groups (O=C–O) may from EPS, was evidence of the accumulation of organic acids, the common bacterial metabolites entrapped within the biofilm58. The generated EPS and FeS indicated that sulfate-reducing bacteria may be involved in the MIC process at the macrofouling/steel interface.
XPS spectra of the rust layer formed at macrofouling/steel interface after nine months of immersion. a Survey scan, b Fe 2p high-resolution spectra, c O 1s high-resolution spectra, d S 2p high-resolution spectra, and e C 1s high-resolution spectra of the specimens OY-RU, AS-RU, and SW-RU. OY-RU, the rust layer or biofilm at the oyster/steel interface; AS-RU, the rust layer or biofilm at the ascidian/steel interface; SW-RU, the rust layer or biofilm at the steel interface which not covered by macrofouling.
To further explore FeS was produced at macrofouling/steel interface, the rust layer was characterized using a Fourier transform infrared (FT-IR) spectrometer, and the resulting spectrum was examined for characteristic vibrational modes corresponding to different corrosion products (Fig. 3a). The results confirmed the presence of magnetite Fe3O4, GR(SO42−), lepidocrocite γ-FeOOH, akageneite β-FeOOH, goethite α-FeOOH, and mackinawite FeS. The peak at 1020 cm−1 was identified as the Fe–O vibrational mode of γ-FeOOH3,59,60,61, the peaks at 795 and 885 cm−1 were found to be from α-FeOOH3,59,60,61, while the peaks at 420, 665, and 840 cm−1 were assigned to β-FeOOH3,47,61,62,63. The typical Fe–O bond peaks of Fe3O4 were observed at 463 and 570 cm−1 3,61,64. In addition, peaks at 1021 and 1117 cm−1 were assigned to FeS3,61,65,66, while the peaks at 660 cm−1 were attributed to GR(SO42−)3,61,67,68. The spectral bands in the range of 1400–1450 cm−1 corresponded to the symmetric stretching of C=O and deformation of O–H in COOH from proteins and polysaccharides, which have been previously reported as the primary constituents of biofilms involved in MIC65,69. The presence of FeS and biofilms further supports the growth of SRB at moacrofouling/steel interface.
a FT-IR spectra and b XRD spectrum of the rust layer formed at macrofouling/steel interface after nine months of immersion. OY-RU, the rust layer or biofilm at the oyster/steel interface; AS-RU, the rust layer or biofilm at the ascidian/steel interface; SW-RU, the rust layer or biofilm at the steel interface which not covered by macrofouling.
XRD spectrum analysis was also performed on the rust layer (Fig. 3b). The results also showed that Fe3O4 (ICCD file 76-0958), GR(SO42−) (ICCD file 13-0092), γ-FeOOH (ICCD file 74-1877), α-FeOOH (ICCD file 08-0098), and β-FeOOH (ICCD file 08-0098) were the major corrosion products in the seawater immersion environment70,71. However, at the macrofouling-covered interface, the growth of SRB led to the formation of FeS (ICCD file 37-0477).
Amplicon sequencing was conducted to understand the differences and dynamics of the microbial communities over time in the rust and biofilms on the steel surfaces. Using the Illumina NovaSeq sequencing platform, we obtained a total of 911,800 effective tags and 19,201 operational taxonomic units (OUTs, 97% similarity) from specimens AS-RU, OY-RU, OYS, OYT, and SW-RU (Supplementary Table 1), detecting a total of 934 genera. After analyzing the 19,201 OUTs and taking the average of parallel specimens, the flower figure and Venn diagram were obtained (Fig. 4), which showed that there were 159 OUTs shared by the five specimens. The OUTs of SW-RU were the highest, with value of 4816. Followed by OY-RU and AS-RU, with values of 1410 and 814, respectively. It meant the rusty environment was favorable for microbial growth, corresponding to the higher abundance of microbial communities. In contrast, the abundance of microbial communities of oyster secretions was the lowest.
a Flower figure and b Venn diagram. OY-RU, the rust layer or biofilm at the oyster/steel interface; AS-RU, the rust layer or biofilm at the ascidian/steel interface; SW-RU, the rust layer or biofilm at the steel interface which not covered by macrofouling; OYS, the biofilm in oyster's secretion; OYT, the biofilm in oyster's tissue.
The α diversity of the specimens AS-RU, OY-RU, OYS, OYT, and SW-RU were analyzed to show the microbial community diversity.
The abundance and diversity index of microbial communities in biofilms and each environment were obtained (Fig. 5a and Supplementary Table 1). The values of Chao1, Ace, Shannon indexes, indices, and OTUs sorted from largest to smallest were: SW-RU > OY-RU > AS-RU > OYT > OYS. These indexes reflected information on community abundance and diversity, indicating that the microbial communities on the steel surface without macrofouling coverage had the highest abundance and diversity among the three rust layer specimens (SW-RU, OY-RU, and AS-RU). Macrofouling coverage indirectly led to a decrease in the microbial communities’ abundance and diversity in the rust layer. By comparing the interfacial corrosion states of the three specimens (Fig. 1), it was believed that only a few corrosive microorganisms played key roles in the MIC process. Notably, the OYS specimen had the lowest microbial community abundance and diversity of the three specimens associated with oysters (OY-RU, OYS, and OYT). Figure 5b showed the p-values for Shannon and Chao1 indices obtained using analysis of variance followed by Tukey-Kramer multiple comparison tests. These differences were statistically significant (p values < 0.05), indicating that the microbial communities in the rust specimens (SW-RU, AS-RU, and OY-RU) were more complex. As the rust layer was covered by macrofouling, the microbial community in the rust layer changed differentially with the gradient of oxygen concentration, and such differences in microbial diversity reflected the ecosystem at the covered interface.
Alpha diversities estimators of microbial communities in each environment. a The Chao1 indices, ACE indices, Shannon indices, and observed OTUs box plots of α-diversity estimators for groups AS-RU, OY-RU, OYS, OYT, and SW-RU. The line in the middle of the box, top and bottom of the box, and whiskers represent the median, 25 and 75 percentiles, and min-to-max values, respectively. Error bars represent standard deviations of triplicate samples. b p-values for Shannon and Chao1 indices obtained using analysis of variance followed by Tukey-Kramer multiple comparison tests. The red backgrounds represent pairs with p-values < 0.05.
In addition, the rarefaction curve and rank abundance curve of 16S rRNA genes could also be used to describe the diversity of specimens (Supplementary Fig. 1). For the rarefaction curve, a flattening curve means that the amount of sequencing data is gradually reasonable, that is only a small number of new species will be generated even with more data. Rank abundance intuitively reflects the richness and evenness of species in the specimen. In the horizontal direction, the higher the species richness, the larger the span of the curve on the x-axis; in the vertical direction, the smoother the curve, the more uniform the distribution of species. As can be seen from the rarefaction curve (Supplementary Fig. 1a), the OUT Number of the rarefaction curve sorted from largest to smallest were: SW-RU > OY-RU > AS-RU > OYT > OYS, showing the same trend as Fig. 5 and Supplementary Table 1. But the curve for SW-RU specimen was not stable with more sequence number, which suggested that the diversity of bacteria of SW-RU specimen was much greater than expected. Even though the SW-RU specimens had the highest microbial abundance and diversity, their species uniformity was lower than that of the AS-RU and OY-RU specimens, as shown in rank abundance curve (Supplementary Fig. 1b). The most uneven species distribution of the OY-RU specimens also reflected that the special environment covered by the calcareous shell would lead to large differences in microbial communities.
The β diversity of the specimens AS-RU, OY-RU, OYS, OYT, and SW-RU were analyzed to compare and analyze the microbial community composition between different specimens.
The non-metric multidimensional scaling (NMDS) analysis result based on the OTUs level was used to reflect the degree of difference between specimens AS-RU, OY-RU, OYS, OYT, and SW-RU through the distance between points (Fig. 6a), which can better reflect the nonlinear structure of ecological data72. From the NMDS results, it could be seen that the specimens OYT and OYS had obvious similarities, while specimen OY-RU and AS-RU had obvious similarities. The specimen SW-RU had a long distance, which further proved that the coverage of macrofouling leaded to the change of the microbial communities in the rust layer.
a Non-metric multidimensional scaling (NMDS) diagram of Bray-Curtis distances and b UPGMA cluster tree based on Unifrac distance and Unweighted Unifrac distance between specimens AS-RU, OY-RU, OYS, OYT, and SW-RU based on OTUs for bacteria. 1, 2, and 3 represent the three parallel specimens sampled at different sites along the interface of AS-RU, OY-RU, and SW-RU.
The UPGMA cluster tree which based on Unifrac distance and Unweighted Unifrac distance showed the same results (Fig. 6b). Specimen SW-RU contained other microbial communities which shared by the other four specimens, which meant that the special environment of the macrofouling/steel covering interface leaded to the existence of characteristic microbial communities, and macrofouling secretions also shared a part of the microbial communities to a certain extent. Moreover, as the transitions in the macrofouling-covered specimens (OY-RU and AS-RU) were larger than those in the non-covered specimens (SW-RU), there was a correlation between the changes in the microbial community and corrosion progression.
The relative abundance of 16S rRNA gene sequences of specimens OYT, OYS, OY-RU, AS-RU, and SW-RU at the phylum level (Fig. 7a), class level (Fig. 7b), and genus level (Fig. 7c) (relative abundance > 1%) were obtained to analyze the composition of microbial community. A total of 82 phyla, 171 classes, and 934 genera were detected.
Taxonomic composition of the microbial community. a Phylum level, b class level, and c genus level composition analysis of top bacterial 16S rRNA gene sequences (relative abundance>1%) obtained from specimens OYT, OYS, OY-RU, AS-RU, and SW-RU. d The cladogram of discriminatory taxa identified in the rust-related groups (OY-RU, AS-RU, and SW-RU) by LEfSe analysis (Linear Discriminant Analysis (LDA), log score >3.5, P = 0.05). The relative abundance of each taxonomy was the average value of that in triplicates.
The major phyla of microbial communities observed in the five specimens were Proteobacteria (38.6–96.7%), Firmicutes (1.5–96.7%), Cyanobacteria (−10.2%), Bacteroidota (−10.2%), Campylobacterota (−5.3%), Desulfobacterota (−5.3%), Actinobacteriota (−2.7%), Actinobacteria (−3.0%), Verrucomicrobiota (−1.6%), and their relative abundances vary from specimen to specimen (Fig. 7a), e.g., Proteobacteria and Firmicutes were jointly detected from all the specimens, Bacteroidetes shared by the specimens OYT, OY-RU, AS-RU and AS-RU. Except for these three phyla, the rust layer at the macrofouling/steel interface had richer community distribution, which Campylobacterota, Actinobacteria, and Verrucomicrobiota shared by the specimens OY-RU and AS-RU. Notably, OY-RU had phylum Desulfobacterota and Actinobacteria, the coverage environment by the calcareous shell of oysters resulted in a decrease in the relative abundance of Proteobacteria and Bacteroidota in the rust layer, they were replaced by Desulfobacterota. Such differences may be influenced by the oxygen concentration and secretions states. As almost all species of Desulfobacterota are SRBs73,74, proving that the environment at oyster/steel interface was anaerobic. Desulfobacterota has been proved the main bacteria which accelerated localized corrosion, which well explained the FeS generated at the oyster/steel interface, and it was believed that Desulfobacterota is involved in the formation of corrosion pits at the interface to a certain extent. Besides Desulfobacterota, Proteobacteria, and Bacteroidetes had been proved to be the main dominant phyla at the corroded steel surface in the marine environment8. Most microorganisms related to iron and sulfur redox cycles belonged to the Proteobacteria75. Some bacteria in Proteobacteria are very important for the formation of biofilms76. Bacteroidetes was confirmed the dominant phylum in the biofilm on steel surface for short-term immersion in seawater77. Bacteria in Bacteroidetes containes a large number of coding genes, which are good at using biofilms to degrade complex polymers (such as POmp and DOM) to create an anaerobic environment78. Bacteria in Firmicutes and Actinobacteria are mostly found in pipeline environments, including various Gram-positive bacterias which can produce spores to resist dehydration and extreme environments79. Actinobacteria is also one of the important microorganisms in the energy transmission pathway, which can survive in harsh environments and cause pitting corrosion79,80.
Among the top 10 classes ranked according to their relative abundance (Fig. 7b), class Gammaproteobacteri was detected from all the specimens, classes Bacteroidia, Bacilli, and Clostridia shared by the specimens OYT, OY-RU, AS-RU, and SW-RU. Notably, class Alphaproteobacteria shared by rust specimens OY-RU, AS-RU, and SW-RU. Classes Verrucomicrobiae, Campylobacteria, and Acidimicrobiia shared by the specimens covered by macrofouling (OY-RU and AS-RU). Apart from these, OY-RU had classes Cyanobacteriia and Desulfovibrionia. Among these classes, classes Gammaproteobacteria and Alphaproteobacteria belonged to phylum Proteobacteria, classes Bacilli and Clostridia belonged to phylum Firmicutes, class Bacteroidia belonged to phylum Bacteroidota, class Verrucomicrobiae belonged to phylum Verrucomicrobiota, class Campylobacteria belonged to phylum Campylobacterota. According to the statistics, Alphaproteobacteria and Gammaproteobacteria accounted for 75% among the cultivable corrosive bacteria.
The exposure of steel in seawater and macrofouling's coverage resulted in the different formation of rust layer and biofilm between the steel surface and the macrofouling/steel interface. The results indicated marked changes in the microbial composition, even at the genus level (Supplementary Table 2 and Fig. 7c). We focused on the top OTUs in each specimen with the relative abundance > 1%. This covered 76.5%, 94.3%, 31.1%, 39.1%, and 52.2% in specimens OYT, OYS, OY-RU, AS-RU, and SW-RU, respectively.
Usually, after microorganisms colonized the steel surface, the exopolysaccharides secreted by them would react with the organic and inorganic substances on the metal surface to form extracellular polymeric substances (EPS). The bacteria then attached to the metal surface together with EPS to form a biofilm. A major feature of biofilms is that their internal pH, dissolved oxygen (DO), ion concentration and organic content are very different from those of seawater. Generally, most marine bacteria with corrosion ability are participants in the cycle process of iron, sulfur, and other elements, and they participate in the corrosion process by changing the cathodic and anodic reaction processes on the metal surface. According to bacterial species and metabolic characteristics, the main corrosive bacteria in the ocean can be divided into sulfate-reducing bacteria (SRB), iron-oxidizing bacteria (IOB), iron-reducing bacteria (IRB), acid-producing bacteria (APB), and slime-producing bacteria (SPB), etc.
By comparing the rust biofilm specimens (SW-RU, AS-RU, and OY-RU), we found genera Woeseia, Pseudomonas (SPB), Comamonas, Ruegeria (SPB), Brevundimonas, Desulfovibrio (SRB), Desulfobulbus (SRB), and archaea Candidatus_Nitrosopumilus finally increased, but genera Pseudoalteromonas, Methyloversatilis (NRB), and Lactobacillus decreased with the macrofouling's coverage.
Desulfovibrio and Desulfobulbus are typical SRB81. SRB are heterotrophic bacteria that can directly obtain electrons from metal substrates to maintain their own life activities. SO42− were reduced to S2− due to the action of SRB, leaving a typical corrosion product FeS at macrofouling/steel interface, which was consistent with the detection of FeS in the rust layer (Fig. 2). Desulfovibrio belonging to class Deltaproteobacteria was observed as the predominant genus in the rust layer in the marine corrosion environment and has been proven to be the main cause of marine MIC7,13,82. Brevundimonas belonging to class Alphaproteobacteria was one of the main microorganisms that could cause corrosion to structural steel80. Woeseia was one of the facultative anaerobic microbes, which comprised facultative anaerobic, gram-negative, oxidase-negative, and catalase-positive chemoheterotrophic marine microbes83. Functional microbial groups with facultative respiration mode was regarded as typical characteristics of mature biofilms in marine environments32. Biofilm-forming genera like Pseudomonas and Ruegeria dominated the surface biofilm were typical SPB. These organisms can generate an anaerobic and acidic environment. The extracellular polymer of Lactobacillus could change of the stability of rust layer by transfering the crystals of the carbon steel interface, which could decrease the corrosion rate of carbon steel84. Notably, the abundance of Pseudoalteromonas decreased substantially with the macrofouling's coverage. This corresponded to an increase in the abundance of Desulfovibrio. Wu et al.85 studied the corrosion of Desulfovibrio and Pseudoalteromonas on low carbon steel Q235 in natural seawater, and found that Pseudoalteromonas depleted DO in seawater, which provided the basic conditions for Desulfovibrio's life activities and caused microbial corrosion. The depletion of DO changed the dominant bacteria in the rust layer from aerobic bacteria to anaerobic bacteria, so that the steel surface began to be affected by MIC. Methyloversatilis was observed as one of the NRB, was proved to play an important role in MIC process of the carbon steel in synthetic bentonite pore water86. Comamonas was found in natural gas pipelines, which was one of the most frequently encountered bacterialand also involved in corrosion process87. In the case of archaea, Candidatus_nitrosopumilus belonging to class Nitrososphaeria occupied a significant position at the macrofouling/steel interface. Members of this genus chemoautotrophically grew nitrite by aerobic oxidation of ammonia and had a high specific affinity for reduced nitrogen, which ensured that they successfully compete with heterotrophic bacterioplankton and phytoplankton. Previous studies have shown that bacteria primarily contribute to surface colonization, while archaea are rarely found. However, in the present study, archaeal members were identified from the macrofouling overlay interface. Their role in macrofouling-influenced corrosion should be re-evaluated.
LEfSe was further employed to identify specific taxa that were enriched in the rust-related specimens (Fig. 7d) and oyster-related specimens (Supplementary Fig. 2). It could be seen from the results that family Desulfurivibrionaceae including Desulfovibrio was enriched in specimen OY-TU among the rust-related specimens, which further proved its important role in oyster/steel interface microbial community herein.
Taken together, the macrofouling's coverage on the steel surface caused different but persistent impacts on the composition of the original microbial community compared to the rust biofilm formed by the corrosion process of steel in the seawater environment. In the otherwise nutrient-poor seawater environment, the protein and polysaccharide contained in macrofouling secretions provided the energy required for microbial growth, which stimulated the growth of microorganisms initially attached to the steel surface. Afterwards, along with the formation of an overlying anoxic environment, the abundance of anaerobic bacteria began to increase (represented by SRB), accompanied by a shift in the diversity of microbial communities. The secretion of macrofouling organisms provides carbon source for the growth of SRB. Carbon source are nutrients used as source of carbon for the formation of microbial cells and carbon-containing metabolites. It has been demonstrated that carbon sources play a crucial role in the MIC process promoted by SRB88,89,90,91,92,93,94. The study by Liu et al.89 indicated that SRB can survive and grow well under organic carbon source starvation. Moreover, the longer the biofilm culture time, the faster the corrosion rate of the steel. They also studied the corrosion inhibition of steel caused by imidazoline derivative in the presence of SRB with organic carbon starvation was investigated in CO2-saturated seawater, found that the corrosion was inhibited by SRB with a high initial count in the absence of organic carbon. However, when the initial count of SRB decreased, the corrosion rate was accelerated88. Zhao et al.92 investigated the impact of different carbon sources on sulfidogenic bacterial communities during the start-up phase of acidogenic sulfate-reducing bioreactors. They observed that the 16S rRNA gene diversity of the dominant bacterial communities in each bioreactor tended to increase when using lactate, acetate/ethanol, glucose, and molasses as carbon sources.
To better identify the shift in microbial community function under macrofouling's coverage conditions, we analyzed function genes using PICRUSt prediction (Fig. 8). The effects of oysters on the interface (Fig. 8a), the effects of ascidians on the interface (Fig. 8b), and the effects of oyster secretions (Fig. 8c) were considered separately. It was found that the microbial community at the macrofouling/steel interface responded differently compared to steel surfaces without macrofouling's coverage (Fig. 8a, b). For oyster covered interface (Fig. 8a), genetic information processing ribosome biogenesis and membrane transport processing phosphotransferase system (PTS) were inhibited by covered hypoxic environment, accompanied by the metabolism oxidative phosphorylation was strongly stimulated; For ascidian-covered interface (Fig. 8b), amino acid metabolism (such as valine, leucine and isoleucine degradation, tryptophan metabolism, phenylalanine metabolism and lysine degradation), lipid Metabolism fatty acid metabolism, energy metabolism (such as oxidative phosphorylation, methane metabolism, and carbon fixation pathways in prokaryotes), xenobiotics biodegradation and metabolism caprolactam degradation, metabolism of terpenoids and polyketides geraniol degradation, and biosynthesis of other secondary metabolites (butirosin and neomycin biosynthesis and betalain biosynthesis) were strongly stimulated, accompanied by the Genetic Information Processing Ribosome Biogenesis and Membrane Transport Processing Phosphotransferase system (PTS) were also inhibited. It could be seen that the macrofouling's coverage had a certain impact on the functional pathways of the microbial community in the rust biofilm. In addition, the role of macrofouling's secretions couled not be ignored (Fig. 8c). As can be seen, membrane transport (such as transporters and ABC transporters) was greatly promoted during the formation of interfacial rust biofilm.
Potential functions of the microbial communities using PICRUSt prediction. The functional pathways of the microbial community by compared the groups a with/without oysters’ coverage, b with/without ascidians’ coverage, c and the microbial community from oyster secretion to the rust. The left column showed the relative abundance of each pathway and the right column showed the difference between groups. Error bars represent standard deviations of triplicate samples. d The abundance of important function genes related to terminal electron acceptation of the microbial community, the function of these genes can be found from Supplementary Table 3. Significant differences (P < 0.05) were analyzed by the T-test.
Macrofouling's coverage changed the functional pathways of the microbial community in the rust biofilm. Thus, the key function genes related to terminal electron acceptation were further identified (Fig. 8d). It was observed that the genes related to oxygen respiration (coxA-D and ccoN-Q), denitrification (nar and napF-H), iron (mtr and mtrA-C), sulfate reduction (dsrA,B and cysI,J) were identified in all the specimens. Not surprisingly, the key gene dsrA and dsrB related to dissimilatory sulfate-reduction process were significantly stimulated in oyster covered specimens (OY-RU) (P < 0.05) compared to specimens AS-RU and SW-RU due to the covered anoxic environment (especially in the area covered by the oyster calcareous shell), which was consistent with the taxonomic analysis (Fig. 7). In contrast, key genes involved in assimilative sulfate reduction, such as cysI and cysJ, were reduced in specimen OY-RU (P < 0.5). Since the sulfate consumption of the oyster/steel interface was greater than that of the ascidian/steel interface, and greater than that of the non-fouling coverage interface. We believed that SRB reduction dissimilatory sulfate is one reason why sulfate consumption is important. Sulfate reduction by microbial assimilation could greatly facilitate the depletion of sulfate covering the anoxic interface (oyster/steel interface).
In addition to the function genes related to sulfate, this rule was also reflected in function genes such as napH, napG, nar, coxC, ccoN, ccoO, ccoP, and ccoQ. The napH, napG, and nar gene were significantly enriched (P < 0.05), and gens coxC, ccoN, ccoO, ccoP, and ccoQ were significantly reduced (P < 0.05) in rust biofilms at oyster/steel interface (OY-RU). This observation indicated that oyster covered anoxic interface stimulated the microbial denitrification, but weakened the oxygen respiration process of the microbial communities. The enhancement of the anaerobic respiration modes on steel surface was because of the formation of heterogeneous anaerobic microenvironments within the thickening and complicated rust layer, where the anaerobic areas existed. The microbial denitrification process could happen under such anaerobic conditions, which had been observed in anoxic marine environments7,95,96.
In marine environment, macroorganism or microorganisms can produce localized attack as pitting, crevice corrosion at metal surface, various antifouling means are used to prevent this from happening97,98. In this study, large differences in the composition and diversity of microbial communities were observed in steel surfae-rust with/without maocrofouling covered when we placed specimens in seawater at the same location for nine months. Meanwhile, interface morphology observation results demonstrated that the adherent oysters and ascidians had caused complex marine corrosion of fouled steel surface, manifested as local corrosion at oyster/steel interface, while the uniform corrosion at ascidian/steel interface. And the rust composition results showed that in addition to goethite, akageneite, lepidocrocite, magnetite, and GR(SO42−), mackinawite was only generated at macrofouling/steel interface. All of these impled that MIC had occurred at the macrofouling/steel interface, and the SRB were involved in the accelerated corrosion process. Therefore, we conducted a comparative study on the composition and potential functions of the microbial community in the macrofouling-covered interface-rust. The three sets of specimens SW-RU, OY-RU, and AS-RU provided data support for the quantitative analysis of the microbial community in the macrofouling-covered interface rust layer biofilm and the contribution of the microbial community to the interface corrosion process.
Our early results showed that for oyster covered interface, due to the existence of the "shadowing effect", the tightly adhered oyster calcareous-shell hindered the diffusion of oxygen and substances at the tightly-covered-area of the interface, leading to the formation of an oxygen concentration cell, thereby further accelerating the corrosion rate at where the crevice has formed3. The most critical of this process not only determined the cathodic process of metal corrosion, but also determined the composition of microorganisms in the rust-biofilm due to the change of oxygen concentration. In this research, compared to specimen not covered by macrofouling (SW-RU), different microbial communities and significant localized corrosion were observed in the rust layer biofilms on the oyster covered interface (OY-RU) (Fig. 1), strongly suggesting that such corrosion was related to MICs. With oysters covered the steel surface, SRB was easily enriched in this environments because of the high concentrations of sulfate ions82,99, which was proved by the enchired SRB (Fig. 7) and key corresponding gene dsr (Fig. 8). The high sulfate consumption and high microbial sulfate-reduction at oyster/steel interface rust biofilms which meant the anaerobic environments for SRB was created due to the "shadowing effect" of the calcareous shell. SRB-induced MIC promoted the formation and development of corrosion pits, which induced the reduction of sulfate in seawater, and accompanied by FeS generation. We hence proposed that in corrosion processes affected by oyster, the SRB was not the main reason for the occurrence of MIC of steel in seawater until the oyster larvae began to colonize at the rusted steel surface. During oyster colonization, biofilm-forming genera (SPB) Pseudomonas and Ruegeria firstly attached to the steel surfaces and formed the biofilm. After oysters colonized the steel surface with the formation of localized anaerobic zones and heterogeneous microenvironments in the covered area, SRB- and SPB-associated bacteria proliferated and promoted the transition of rust biofilms (Fig. 7). These could be explained why anaerobic NO3− reduction-related genes were significantly enriched (P < 0.05), and gens coxC, ccoN, ccoO, ccoP, and ccoQ were significantly reduced (Fig. 8d), accompanied by SRB enrichment at oyster overlay interfaces (Fig. 7). These factors accelerated the crevice corrosion at oyster/steel interface.
Nobly, these phenomena did not lead to the same crevice corrosion at the ascidian/steel interface. This can be explained by the abundance of dominant microorganisms and the differences in oxygen concentration at the ascidian/steel and oyster/steel interfaces. Beneath the covered ascidian was still an aerobic environment due to the conductivity- and ion-diffusivity ability of ascidian's body. High concentration of oxygen leaded to the low activity of SRB, so SRB is rarely involved in the MIC process at the ascidian/steel interface. Conversely, the existing gaps at the oyster/steel interface and nutrients provided by secretions resulted in a high activity of SRBs, which caused the severe MIC at specific sites.
In summary, field experiments, laboratory characterizations, and high-throughput sequencing technology were utilized to investigate potential microbial communities at the macrofouling/steel interface, which can lead to severe microbiologically influenced corrosion (MIC). The study found that the microecological environment covered by macrofouling, as well as the nutrient source provided by macrofouling secretions, stimulated the abundance and diversity of microbial communities at the interface. Specifically, sulfate-reducing bacteria (SRB) were found to be involved in the MIC process. MIC processes were found to differ significantly between hard-fouling and soft-fouling covered interfaces. In comparison to ascidians, the oyster/steel interface created a local anaerobic zone due to the low-ionic-diffusivity of the oyster's calcareous shell. This anaerobic environment stimulated the growth of SRBs, leading to higher FeS content and severe localized corrosion. Notably, the SRBs Desulfovibrio and Desulfobulbus, as well as the SRB-related function gene dsr, were increased, while the oxygen-related function gene coxC, ccoN, ccoO, ccoP, and ccoQ were found to decrease.
The paper did not provide data to support the hypothesis that higher microbial abundance and diversity directly promote steel corrosion. Surprisingly, the study found that steel surfaces without macrofouling coverage had the richest microbial communities, yet experienced less severe MIC. We believed that only a small fraction of the numerous microbial communities present was actually involved in the interfacial MIC process, with SRB playing a key role. The microbial community differences due to changes in the local microenvironment and the growth of anaerobic bacteria should be paid attention to during the MIC process. Doing so will help us better understand the localized corrosion mechanism at the interface and accurately quantify the specific contribution of microorganisms in complex corrosion processes.
High-strength low-alloy steel (AISI 4135, Shougang New Steel Co., Ltd, China) was selected as test steel in this work, which with the following element composition (in wt%): C 0.399, S 0.0144, P 0.0146, Si 0.293, Mo 0.204, Mn 0.509, Ni 0.0804, Cr 0.903, and Fe balance. Cylindrical specimens with a diameter of 1 cm and thickness of 1 cm were chosen and embedded in resins, exposing a surface area of 0.785 cm2 (Fig. 9a). These specimens were then immersed in the seawater below the low tide line, where macrofouling was more likely to adhere. The field exposure site was located off a pier in Jiaozhou Bay, Qingdao, China (N 120°15′4″, E 35°59′11″)). After nine months of immersion in seawater from March 1, 2021 to December 1, 2021, the cylindrical specimen which covered by an oyster (Fig. 9b), covered by ascidians (Fig. 9c), and not covered by macrofouling (Fig. 9d) were retrieved. Because the attachment of macrofouling organisms is uncontrollable, the experimental design is as follows: multiple parallel specimens were hung at the same location, and the coverage of macrofouling was observed at regular intervals. After identifying some specimens with oyster and ascidian attachment, they were selected as target specimen. After a period of time, the target specimens with oyster and ascidian attachment were collected separately, and specimens without macrofouling attachment were also chosen and collected as the control group. Then, in-situ rust layers and biofilms were collected at the macrofouling/steel interface for further sequencing and rust compositional analysis. After collecting the specimen, all the rust specimens and biofilm were transferred to sterile centrifuge tubes100. Three parallel specimens were collected at different points and were assigned SW-RU (the rust layer or biofilm at the steel interface which not covered by macrofouling), AS-RU (the rust layer or biofilm at the ascidian/steel interface), OY-RU (the rust layer or biofilm at the oyster/steel interface), OY (the rust layer or biofilm in oyster secretions), and OYT (the rust layer or biofilm in oyster tissues). For rust specimens (SW-RU, OY-RU, and AS-RU), first removed the covered macrofouling from the steel substrate surface, and then collect the rust layer and biofilms with sterile forceps. For OYS and OYT specimens, first used sterile forceps to pry open the oyster shell. Then, used a sterile pipette to collect the oyster secretions (OYS) and used a sterile surgical blade to cut and collect the oyster tissues (OYT). All collected specimens were kept in an ice box, transported to the laboratory as soon as possible, and stored at −20 °C for further analysis.
a Cylindrical specimen; b–d Cylindrical specimen b covered by an oyster, c covered by ascidians, and d not covered by macrofouling after nine months of immersion in seawater.
For macrofouling/steel interface morphology observation and rust layer analysis, the covered macrofouling were removed first and then the rust composition and morphology characterization of macrofouling/steel interface were carried out. The morphology of the rust-covered steel surface after removing the macrofouling was investigated by scanning electron microscopy (SEM, Regulus 8100, Hitachi, Japan). The rust-removed steel surface was observed by a 3D measuring laser microscope (LSCM, LEXT 3D OLS5000, Olympus, Japan) after removed the rust layer by using 20 vol% hydrochloric acid with 1 vol% hexamethylenetetramine. The collected rust layer was mixed with glycerol and freeze-vacuum dried to avoid oxidation and kept in vacuum containers. X-ray photoelectron spectroscopy (XPS, EscaLab 250Xi, Thermo Fisher Scientific, America), X-ray diffraction (XRD, Ultima IV, Rigaku, Japan), and Fourier transform infrared spectroscopy (FT-IR, Nicolet iS10, Thermo Fisher Scientific, USA) techniques was used for rust characterization. For XPS analysis, the XPS data were collected using a Thermo Fisher ESCALAB 250Xi spectrometer with monochromatic Al Kα radiation and argon-assisted charge compensation. A step size of 0.05 eV, dwell time of 100 ms, and pass energy of 10 eV were used for the detailed spectra. Calibration was conducted to eliminate voltage-induced alterations in electron spectra. The spectra were recorded at a take-off angle of 90° and all binding energies were charge-corrected to the C 1s signal, which was set at 284.6 eV. For the characterization of the iron oxides, high-resolution scans of the C 1s, S 1s, O 1s, and Fe 2p peaks were acquired. For XRD analysis, the rust samples were characterized using a Rigaku XRD diffractometer with a Cu Kα radiation (λ = 1.5406 Å). The diffraction data were collected over a 2θ range of 5–90° with a scanning rate of 5°/min. For FT-IR analysis, the rust sample was ground into a fine powder and pressed into a disc using spectroscopically pure dry KBr under vacuum. Spectra was collected over a range of wavelengths (400–4000 cm−1) at a resolution of 2 cm−1. Background spectra was collected prior to each individual sample.
DNA extracted from the specimens by the SDS method was used for sequencing, then agarose gel electrophoresis was used to check the purity and concentration of DNA. Specific primers with Barcode, Phusion® High-Fidelity PCR Master Mix with GC Buffer (New England Biolabs, England), and high-efficiency high-fidelity enzymes were used for PCR amplification101. 16S rRNA genes were amplified using the primer sets 515F/806R. The integrity and approximate length of the DNA were examined by 2% agarose gel electrophoresis, and PCR products were purified with a PCR purification kit (QIAGEN, Hilden, NRW, Germany)102,103. The PCR libraries were conducted using TruSeq® DNA PCR-Free specimen Preparation Kit (Illumina, San Diego, CA). After quantification with Qubit and Q-PCR quantification, the qualified PCR libraries were sequenced on the Illumina NovaSeq6000 platform.
After truncating the Barcode and primer sequences according to the Barcode sequence and PCR amplification primer sequence, FLASH (V1.2.7) was used to splice the reads of each specimen to obtain raw tags104. The quality control was performed on the raw tags (sequence length is 200 to 10,000 base pairs, consecutive identical base pairs N < 6; fuzzy bases N < 1, Q < 25), then the Fastp software was used to filter the spliced raw tags to obtain clean tags. After removing chimeric sequences, the fine effective tags were obtained105. For OTU subsequent diversity index and abundance information analysis, the Uparse algorithm (Uparse v7.0.1001)106 was used to cluster all effective tags of all specimens and the sequences were clustered into OTUs (operational taxonomic units) with 97% sequence similarity. Species annotation was performed on OTUs sequences, and species annotation analysis was performed using the Mothur method and the SSUrRNA database (SILVA138.1)107,108 to obtain taxonomic information and community composition at each taxonomic level: kingdom, phylum, class, order, family, genus, species.
The alpha diversity index (α diversity) was used to indicate the microbial community diversity within specimens. QIIME calculation and R software were used to cover the sequencing depth109. Observed-otus, Chao1, Shannon, Simpson, and ACE indices were calculated using QIIME software (Version 1.9.1), and dilution curves and rank abundance curves were drawn using R software (Version 2.15.3)110. The beta diversity index (β diversity) was used to analyze the microbial community composition of different specimens. Based on the weighted non-ifrac distance, the Bray-Curtis distance based on OTU was drawn from the non-metric multidimensional scaling (NMDS)111,112. UPGMA cluster analysis was performed with weighted unifrac distance matrix and unweighted unifrac distance matrix. The clustering results were integrated and displayed with the relative abundance of species at the phylum level in each specimen113,114. Applied PCA analysis to extract two axes that best reflect the differences between specimens111. The unifrac distance was calculated by QIIME software (Version 1.9.1), and the UPGMA specimen clustering tree was constructed. PCA and NMDS plots were also drawn using R software (Version 2.15.3). The potential function genes were annotated against KEGG database using PICRUSt prediction115,116. The cladogram of discriminatory taxa was identified in the rust-related groups by the linear discriminant analysis (LDA) based on Kruskal−Wallis with log score >3.5 and P = 0.05 using LEfSe software (V1.0)7,117. The relative abundance of each taxonomy was the average value of that in triplicates. T-test was used to determine the difference in individual function genes between different treatments7.
The data that support the findings of this study are available from the corresponding author upon reasonable request. Sequencing data of the 15 specimens obtained were deposited in the NCBI Short Read Archive (SRA) database under Bioproject accession number PRJNA865886, with Biospecimen numbers SAMN 30139936–30139950.
Guenther, J., Walker-Smith, G., Waren, A. & De Nys, R. Fouling-resistant surfaces of tropical sea stars. Biofouling 23, 413–418 (2007).
Article CAS Google Scholar
Myan, F. W. Y., Walker, J. & Paramor, O. The interaction of marine fouling organisms with topography of varied scale and geometry: a review. Biointerphases 8, 30 (2013).
Article Google Scholar
Wang, Z. Q., Huang, Y. L., Wang, X. T., Xu, Y. & Cai, F. F. Effects of oyster as macrofouling organism on corrosion mechanisms of a high-strength low-alloy steel. Corros. Sci. 207, 110580 (2022).
Article CAS Google Scholar
Li, Y. F. & Ning, C. Y. Latest research progress of marine microbiological corrosion and bio-fouling, and new approaches of marine anti-corrosion and anti-fouling. Bioact. Mater. 4, 189–195 (2019).
Article Google Scholar
Permeh, S., Lau, K., Boan, M. E. & Duncan, M. Influence of macro-and microfouling on corrosion of steel bridge piles submerged in natural waters. J. Mater. Civ. Eng. 33, 04021105 (2021).
Article CAS Google Scholar
De Brito, L. V. R., Coutinho, R., Cavalcanti, E. S. & Benchimol, M. The influence of macrofouling on the corrosion behaviour of API 5L X65 carbon steel. Biofouling 23, 193–201 (2007).
Article Google Scholar
Zhang, Y. M. et al. Microbiologically influenced corrosion of steel in coastal surface seawater contaminated by crude oil. npj Mater. Degrad. 6, 35 (2022).
Article CAS Google Scholar
Zhang, Y. M. et al. Analysis of marine microbial communities colonizing various metallic materials and rust layers. Biofouling 35, 429–442 (2019).
Article CAS Google Scholar
Lanneluc, I. et al. On the bacterial communities associated with the corrosion product layer during the early stages of marine corrosion of carbon steel. Int. Biodeterior. Biodegrad. 99, 55–65 (2015).
Article CAS Google Scholar
Cheng, S. et al. Microbially influenced corrosion of stainless steel by marine bacterium Vibrio natriegens: (I) Corrosion behavior. Mater. Sci. Eng. C. 29, 751–755 (2009).
Article CAS Google Scholar
Khan, M. S. et al. Microbiologically influenced corrosion of titanium caused by aerobic marine bacterium Pseudomonas aeruginosa. J. Mater. Sci. Technol. 35, 216–222 (2019).
Article CAS Google Scholar
Venzlaff, H. et al. Accelerated cathodic reaction in microbial corrosion of iron due to direct electron uptake by sulfate-reducing bacteria. Corros. Sci. 66, 88–96 (2013).
Article CAS Google Scholar
Duan, J. Z. et al. Corrosion of carbon steel influenced by anaerobic biofilm in natural seawater. Electrochim. Acta 54, 22–28 (2008).
Article CAS Google Scholar
Enning, D. & Garrelfs, J. Corrosion of iron by sulfate-reducing bacteria: new views of an old problem. Appl. Environ. Microbiol. 80, 1226–1236 (2014).
Article Google Scholar
Dinh, H. T. et al. Iron corrosion by novel anaerobic microorganisms. Nature 427, 829–832 (2004).
Article CAS Google Scholar
Dou, W. W. et al. Biocorrosion of copper by nitrate reducing Pseudomonas aeruginosa with varied headspace volume. Int. Biodeterior. Biodegrad. 171, 105405 (2022).
Article CAS Google Scholar
Chugh, B. et al. Extracellular electron transfer by Pseudomonas aeruginosa in biocorrosion: a review. ACS Biomater. Sci. Eng. 8, 1049–1059 (2022).
Article CAS Google Scholar
Pu, Y. N. et al. Microbiologically influenced corrosion of Cu by nitrate reducing marine bacterium Pseudomonas aeruginosa. J. Mater. Sci. Technol. 47, 10–19 (2020).
Article CAS Google Scholar
Tian, F., He, X. Y., Bai, X. Q. & Yuan, C. Q. Electrochemical corrosion behaviors and mechanism of carbon steel in the presence of acid-producing bacterium Citrobacter farmeri in artificial seawater. Int. Biodeterior. Biodegrad. 147, 104872 (2020).
Article Google Scholar
Chen, S. Q., Deng, H., Liu, G. Z. & Zhang, D. Corrosion of Q235 carbon steel in seawater containing Mariprofundus ferrooxydans and Thalassospira sp. Front. Microb. 10, 936 (2019).
Article Google Scholar
Sun, H. F., Shi, B. Y., Yang, F. & Wang, D. S. Effects of sulfate on heavy metal release from iron corrosion scales in drinking water distribution system. Water Res. 114, 69–77 (2017).
Article CAS Google Scholar
Gu, T. Y., Wang, D., Lekbach, Y. & Xu, D. K. Extracellular electron transfer in microbial biocorrosion. Curr. Opin. Electrochem. 29, 100763 (2021).
Article CAS Google Scholar
Gu, T. New understandings of biocorrosion mechanisms and their classifications. J. Microb. Biochem. Technol. 4, 1 (2012).
Article Google Scholar
Zhou, E. Z. et al. Direct microbial electron uptake as a mechanism for stainless steel corrosion in aerobic environments. Water Res. 219, 118553 (2022).
Article CAS Google Scholar
Jin, Y. T. et al. Sharing riboflavin as an electron shuttle enhances the corrosivity of a mixed consortium of Shewanella oneidensis and Bacillus licheniformis against 316L stainless steel. Electrochim. Acta 316, 93–104 (2019).
Article CAS Google Scholar
Li, Z. Y. et al. Adaptive bidirectional extracellular electron transfer during accelerated microbiologically influenced corrosion of stainless steel. Commun. Mater. 2, 67 (2021).
Article CAS Google Scholar
Kalnaowakul, P., Xu, D. K. & Rodchanarowan, A. Accelerated corrosion of 316L stainless steel caused by Shewanella algae biofilms. ACS Appl. Bio Mater. 3, 2185–2192 (2020).
Article CAS Google Scholar
Tang, H. Y. et al. Stainless steel corrosion via direct iron-to-microbe electron transfer by Geobacter species. ISME J. 15, 3084–3093 (2021).
Article CAS Google Scholar
Reguera, G. et al. Extracellular electron transfer via microbial nanowires. Nature 435, 1098–1101 (2005).
Article CAS Google Scholar
Pham, T. H. et al. Metabolites produced by Pseudomonas sp enable a Gram-positive bacterium to achieve extracellular electron transfer. Appl. Microbiol. Biotechnol. 77, 1119–1129 (2008).
Article CAS Google Scholar
Zhou, E. Z. et al. Accelerated biocorrosion of stainless steel in marine water via extracellular electron transfer encoding gene phzH of Pseudomonas aeruginosa. Water Res. 220, 118634 (2022).
Article CAS Google Scholar
Zhang, Y. M. et al. Metagenomic resolution of functional diversity in copper surface-associated marine biofilms. Front. Microb. 10, 2863 (2019).
Article Google Scholar
Wang, Z. Q., Li, Y. T., Ren, J., Xu, W. C. & Yang, L. H. Investigating the effects of environment, corrosion degree, and distribution of corrosive microbial communities on service-life of refined oil pipelines. Environ. Sci. Pollut. Res. 29, 52204–52219 (2022).
Article Google Scholar
Zhang, G. J. et al. The bacterial community significantly promotes cast iron corrosion in reclaimed wastewater distribution systems. Microbiome 6, 1–18 (2018).
Article Google Scholar
Huttunen-Saarivirta, E. et al. Ennoblement, corrosion, and biofouling in brackish seawater: comparison between six stainless steel grades. Bioelectrochemistry 120, 27–42 (2018).
Article CAS Google Scholar
Staniszewska, A. et al. High-throughput sequencing approach in analysis of microbial communities colonizing natural gas pipelines. Microbiologyopen 8, e00806 (2019).
Article Google Scholar
de Azambuja, A. O. et al. Microbial community composition in Brazilian stored diesel fuel of varying sulfur content, using high-throughput sequencing. Fuel 189, 340–349 (2017).
Article Google Scholar
Procopio, L. The era of ‘omics’ technologies in the study of microbiologically influenced corrosion. Biotechnol. Lett. 42, 341–356 (2020).
Article CAS Google Scholar
Lezzi, M., Del Pasqua, M., Pierri, C. & Giangrande, A. Seasonal non-indigenous species succession in a marine macrofouling invertebrate community. Biol. Invasions 20, 937–961 (2018).
Article Google Scholar
Blackwood, D. J., Lim, C. S., Teo, S. L. M., Hu, X. P. & Pang, J. J. Macrofouling induced localized corrosion of stainless steel in Singapore seawater. Corros. Sci. 129, 152–160 (2017).
Article CAS Google Scholar
Vinagre, P. A., Simas, T., Cruz, E., Pinori, E. & Svenson, J. Marine biofouling: a European database for the marine renewable energy sector. J. Mar. Sci. Eng. 8, 495 (2020).
Article Google Scholar
Jonker, J. L. et al. The chemistry of stalked barnacle adhesive (Lepas anatifera). Interface Focus 5, 20140062 (2015).
Article Google Scholar
Lee, H., Dellatore, S. M., Miller, W. M. & Messersmith, P. B. Mussel-inspired surface chemistry for multifunctional coatings. Science 318, 426–430 (2007).
Article CAS Google Scholar
Lee, H., Scherer, N. F. & Messersmith, P. B. Single-molecule mechanics of mussel adhesion. Proc. Natl Acad. Sci. USA 103, 12999–13003 (2006).
Article CAS Google Scholar
Zhang, G. F. et al. The oyster genome reveals stress adaptation and complexity of shell formation. Nature 490, 49–54 (2012).
Article CAS Google Scholar
Permeh, S., Lau, K., Boan, M. E., Tansel, B. & Duncan, M. Cathodic polarization behavior of steel with different marine fouling morphologies on submerged bridge elements with cathodic protection. J. Mater. Civ. Eng. 32, 04020184 (2020).
Article CAS Google Scholar
Zou, Y., Wang, J. & Zheng, Y. Y. Electrochemical techniques for determining corrosion rate of rusted steel in seawater. Corros. Sci. 53, 208–216 (2011).
Article CAS Google Scholar
Xu, W. C. et al. Accelerated corrosion of 316L stainless steel in simulated body fluids in the presence of H2O2 and albumin. Mater. Sci. Eng. C.-Mater. Biol. Appl. 92, 11–19 (2018).
Article CAS Google Scholar
Guo, S. Q., Xu, L. N., Zhang, L., Chang, W. & Lu, M. X. Corrosion of alloy steels containing 2% chromium in CO2 environments. Corros. Sci. 63, 246–258 (2012).
Article CAS Google Scholar
Wang, Z. Q. et al. Study on inner corrosion behavior of high strength product oil pipelines. Eng. Fail. Anal. 115, 104659 (2020).
Article CAS Google Scholar
Marcus, P. & Grimal, J. M. The anodic dissolution and passivation of NiCrFe alloys studied by ESCA. Corros. Sci. 33, 805–814 (1992).
Article CAS Google Scholar
Tan, B. J., Klabunde, K. J. & Sherwood, P. M. A. X-ray photoelectron spectroscopy studies of solvated metal atom dispersed catalysts. Monometallic iron and bimetallic iron-cobalt particles on alumina. Chem. Mater. 2, 186–191 (1990).
Article CAS Google Scholar
Wren, A. G., Phillips, R. W. & Tolentino, L. U. Surface reactions of chlorine molecules and atoms with water and sulfuric acid at low temperatures. J. Colloid Interface Sci. 70, 544–557 (1979).
Article CAS Google Scholar
Boursiquot, S., Mullet, M. & Ehrhardt, J. J. XPS study of the reaction of chromium (VI) with mackinawite (FeS). Surf. Interface Anal. 34, 293–297 (2002).
Article CAS Google Scholar
Allen, G. C., Curtis, M. T., Hooper, A. J. & Tucker, P. M. X-Ray photoelectron spectroscopy of iron–oxygen systems. J. Chem. Soc. Dalton Trans. 14, 1525–1530 (1974).
Article Google Scholar
Rouxhet, P. G. & Genet, M. J. XPS analysis of bio-organic systems. Surf. Interface Anal. 43, 1453–1470 (2011).
Article CAS Google Scholar
Ramstedt, M., Leone, L., Persson, P. & Shchukarev, A. Cell wall composition of Bacillus subtilis changes as a function of pH and Zn2+ exposure: insights from cryo-XPS measurements. Langmuir 30, 4367–4374 (2014).
Article CAS Google Scholar
Kumar, M. A., Anandapandian, K. T. K. & Parthiban, K. Production and characterization of exopolysaccharides (EPS) from biofilm forming marine bacterium. Braz. Arch. Biol. Technol. 54, 259–265 (2011).
Article CAS Google Scholar
Perez, F. R., Barrero, C. A. & Garcia, K. E. Factors affecting the amount of corroded iron converted into adherent rust in steels submitted to immersion tests. Corros. Sci. 52, 2582–2591 (2010).
Article CAS Google Scholar
Weckler, B. & Lutz, H. D. Lattice vibration spectra. Part XCV. Infrared spectroscopic studies on the iron oxide hydroxides goethite (alpha), akaganeite (beta), lepidocrocite (gamma), and feroxyhite (delta). Eur. J. Solid State Inorg. Chem. 35, 531–544 (1998).
Article CAS Google Scholar
Wang, Z. et al. Macrofouling organisms: protection or damage of steel in marine environments? Corros. Sci. 212, 110928 (2023).
Article CAS Google Scholar
Song, H., Zhang, X., Chen, T. & Jia, X. One-pot synthesis of bundle-like beta-FeOOH nanorods and their transformation to porous alpha-Fe2O3 microspheres. Ceram. Int. 40, 15595–15602 (2014).
Article CAS Google Scholar
Wei, C. & Nan, Z. Effects of experimental conditions on one-dimensional single-crystal nanostructure of beta-FeOOH. Mater. Chem. Phys. 127, 220–226 (2011).
Article CAS Google Scholar
Hu, J. Y., Cao, S. A. & Xie, J. L. EIS study on the corrosion behavior of rusted carbon steel in 3% NaCl solution. Anti-Corros. Methods Mater. 60, 100–105 (2013).
Article CAS Google Scholar
Badica, C. E. & Chirita, P. An electrochemical study of the oxidative dissolution of iron monosulfide (FeS) in air-equilibrated solutions. Electrochim. Acta 178, 786–796 (2015).
Article CAS Google Scholar
Chirita, P., Descostes, M. & Schlegel, M. L. Oxidation of FeS by oxygen-bearing acidic solutions. J. Colloid Interface Sci. 321, 84–95 (2008).
Article CAS Google Scholar
Ona-Nguema, G. et al. Competitive formation of hydroxycarbonate green rust 1 versus hydroxysulphate green rust 2 in Shewanella putrefaciens cultures. Geomicrobiol. J. 21, 79–90 (2004).
Article CAS Google Scholar
Zegeye, A. et al. Formation of hydroxysulphate green rust 2 as a single Iron(II-III) mineral in microbial culture. Geomicrobiol. J. 22, 389–399 (2005).
Article CAS Google Scholar
Ferri, T. Z., Roncevic, S., Vrkljan, G. L. & Konestra, A. Post-depositional alterations of terrestrial and marine finds of Roman ceramics from Crikvenica production centre (NE Adriatic, Croatia)—a contribution towards chemometric classification. J. Cult. Herit. 43, 12–25 (2020).
Article Google Scholar
Refait, P., Grolleau, A. M., Jeannin, M., Francois, E. & Sabot, R. Localized corrosion of carbon steel in marine media: Galvanic coupling and heterogeneity of the corrosion product layer. Corros. Sci. 111, 583–595 (2016).
Article CAS Google Scholar
Refait, P., Jeannin, M., Sabot, R., Antony, H. & Pineau, S. Electrochemical formation and transformation of corrosion products on carbon steel under cathodic protection in seawater. Corros. Sci. 71, 32–36 (2013).
Article CAS Google Scholar
Rivas, M. N. et al. A microbiota signature associated with experimental food allergy promotes allergic sensitization and anaphylaxis. J. Allergy Clin. Immunol. 131, 201–212 (2013).
Article Google Scholar
Waite, D. W. et al. Proposal to reclassify the proteobacterial classes Deltaproteobacteria and Oligoflexia, and the phylum Thermodesulfobacteria into four phyla reflecting major functional capabilities. Int. J. Syst. Evol. Microbiol. 70, 5972–6016 (2020).
Article CAS Google Scholar
Wakai, S. et al. Dynamics of microbial communities on the corrosion behavior of steel in freshwater environment. npj Mater. Degrad. 6, 45 (2022).
Article CAS Google Scholar
Cankovic, M., Petric, I., Margus, M. & Ciglenecki, I. Spatio-temporal dynamics of sulfate-reducing bacteria in extreme environment of Rogoznica Lake revealed by 16S rRNA analysis. J. Mar. Syst. 172, 14–23 (2017).
Article Google Scholar
Park, H. I., Kim, J. S., Kim, D. K., Choi, Y. J. & Pak, D. Nitrate-reducing bacterial community in a biofilm-electrode reactor. Enzym. Microb. Technol. 39, 453–458 (2006).
Article CAS Google Scholar
Oliveira, V. M. et al. Molecular analysis of microbial diversity in corrosion samples from energy transmission towers. Biofouling 27, 435–447 (2011).
Article Google Scholar
Conlette, O. C. Microbial communities of light crude from Nigeria and potential for in situ biodegradation, souring, and corrosion. Pet. Sci. Technol. 34, 71–77 (2016).
Article CAS Google Scholar
Burleigh, T. D., Gierke, C. G., Fredj, N. & Boston, P. J. Copper tube pitting in Santa Fe municipal water caused by microbial induced corrosion. Materials 7, 4321–4334 (2014).
Article CAS Google Scholar
Machuca, L. L., Jeffrey, R. & Melchers, R. E. Microorganisms associated with corrosion of structural steel in diverse atmospheres. Int. Biodeterior. Biodegrad. 114, 234–243 (2016).
Article CAS Google Scholar
Anandkumar, B., George, R. P., Maruthamuthu, S., Palaniswamy, N. & Dayal, R. K. Corrosion behavior of SRB Desulfobulbus propionicus isolated from an Indian petroleum refinery on mild steel. Mater. Corros. 63, 355–362 (2012).
Article CAS Google Scholar
Li, X. H. et al. Analysis of bacterial community composition of corroded steel immersed in Sanya and Xiamen seawaters in China via method of Illumina MiSeq sequencing. Front. Microb. 8, 1737 (2017).
Article Google Scholar
Du, Z. J., Wang, Z. J., Zhao, J. X. & Chen, G. J. Woeseia oceani gen. nov., sp nov., a chemoheterotrophic member of the order Chromatiales, and proposal of Woeseiaceae fam. nov. Int. J. Syst. Evol. Microbiol. 66, 107–112 (2016).
Article CAS Google Scholar
Ignatova-Ivanova, T., Ivanov, R., Iliev, I. & Ivanova, I. Study of anticorrosion effect of EPS from now strains Lactobacillus delbrueckii. Biotechnol. Biotechnol. Equip. 23, 705–708 (2009).
Article Google Scholar
Wu, J. J. et al. The influence of Desulfovibrio sp and Pseudoalteromonas sp on the corrosion of Q235 carbon steel in natural seawater. Corros. Sci. 112, 552–562 (2016).
Article CAS Google Scholar
Shrestha, R. et al. Anaerobic microbial corrosion of carbon steel under conditions relevant for deep geological repository of nuclear waste. Sci. Total Environ. 800, 149539 (2021).
Article CAS Google Scholar
Zhu, X. Y., Lubeck, J. & Kilbane, J. J. Characterization of microbial communities in gas industry pipelines. Appl. Environ. Microbiol. 69, 5354–5363 (2003).
Article CAS Google Scholar
Liu, H. W. et al. Corrosion inhibition behavior of X80 pipeline steel by imidazoline derivative in the CO2-saturated seawater containing sulfate-reducing bacteria with organic carbon starvation. Corros. Sci. 203, 110345 (2022).
Article CAS Google Scholar
Liu, H. W., Gu, T. Y., Zhang, G. A., Liu, H. F. & Cheng, Y. F. Corrosion of X80 pipeline steel under sulfate-reducing bacterium biofilms in simulated CO2-saturated oilfield produced water with carbon source starvation. Corros. Sci. 136, 47–59 (2018).
Article CAS Google Scholar
Zhao, C. R., Chen, N., Liu, T. & Feng, C. P. Effects of adding different carbon sources on the microbial behavior of sulfate-reducing bacteria in sulfate-containing wastewater. J. Clean. Prod. 392, 136332 (2023).
Article CAS Google Scholar
Fan, Y. X. et al. Early corrosion behavior of X80 pipeline steel in a simulated soil solution containing Desulfovibrio desulfuricans. Bioelectrochemistry 141, 107880 (2021).
Article CAS Google Scholar
Zhao, Y. G., Wang, A. J. & Ren, N. Q. Effect of carbon sources on sulfidogenic bacterial communities during the starting-up of acidogenic sulfate-reducing bioreactors. Bioresour. Technol. 101, 2952–2959 (2010).
Article CAS Google Scholar
Zhang, M. L. & Wang, H. X. Organic wastes as carbon sources to promote sulfate reducing bacterial activity for biological remediation of acid mine drainage. Miner. Eng. 69, 81–90 (2014).
Article CAS Google Scholar
Fu, Q. et al. Biologically competitive effect of Desulfovibrio desulfurican and Pseudomonas stutzeri on corrosion of X80 pipeline steel in the Shenyang soil solution. Bioelectrochemistry 145, 108051 (2022).
Article CAS Google Scholar
Zedelius, J. et al. Alkane degradation under anoxic conditions by a nitrate-reducing bacterium with possible involvement of the electron acceptor in substrate activation. Environ. Microbiol. Rep. 3, 125–135 (2011).
Article CAS Google Scholar
Scott, N. M. et al. The microbial nitrogen cycling potential is impacted by polyaromatic hydrocarbon pollution of marine sediments. Front. Microb. 5, 108 (2014).
Article Google Scholar
Zhou, Z. Y. et al. Distinctive roles of graphene oxide, ZnO quantum dots, and their nanohybrids in anti-corrosion and anti-fouling performance of waterborne epoxy coatings. Chem. Eng. J. 439, 135765 (2022).
Article CAS Google Scholar
Zhou, Z. Y. et al. Anti-corrosion and anti-fouling properties of ball-like GQDs hybrided MOFs functionalized with silane in waterborne epoxy-polydimethylsiloxane coatings: experimental and theoretical studies. Appl. Mater. Today 30, 101704 (2023).
Article Google Scholar
Vigneron, A. et al. Complementary microorganisms in highly corrosive biofilms from an offshore oil production facility. Appl. Environ. Microbiol. 82, 2545–2554 (2016).
Article CAS Google Scholar
Lin, W., Yu, Z., Zhang, H. & Thompson, I. P. Diversity and dynamics of microbial communities at each step of treatment plant for potable water generation. Water Res. 52, 218–230 (2014).
Article CAS Google Scholar
Moskovitz, M. et al. Characterization of the oral microbiome among children with type 1 diabetes compared with healthy children. Front. Microb. 12, 756808 (2021).
Article Google Scholar
Di Pinto, A. et al. A comparison of DNA extraction methods for food analysis. Food Control 18, 76–80 (2007).
Article Google Scholar
Guy, R. A., Payment, P., Krull, U. J. & Horgen, P. A. Real-time PCR for quantification of Giardia and Cryptosporidium in environmental water samples and sewage. Appl. Environ. Microbiol. 69, 5178–5185 (2003).
Article CAS Google Scholar
Magoc, T. & Salzberg, S. L. FLASH: fast length adjustment of short reads to improve genome assemblies. Bioinformatics 27, 2957–2963 (2011).
Article CAS Google Scholar
Haas, B. J. et al. Chimeric 16S rRNA sequence formation and detection in Sanger and 454-pyrosequenced PCR amplicons. Genome Res. 21, 494–504 (2011).
Article CAS Google Scholar
Edgar, R. C. UPARSE: highly accurate OTU sequences from microbial amplicon reads. Nat. Methods 10, 996-+ (2013).
Article CAS Google Scholar
Wang, Q., Garrity, G. M., Tiedje, J. M. & Cole, J. R. Naive Bayesian classifier for rapid assignment of rRNA sequences into the new bacterial taxonomy. Appl. Environ. Microbiol. 73, 5261–5267 (2007).
Article CAS Google Scholar
Quast, C. et al. The SILVA ribosomal RNA gene database project: improved data processing and web-based tools. Nucleic Acids Res. 41, D590–D596 (2013).
Article CAS Google Scholar
Caporaso, J. G. et al. QIIME allows analysis of high-throughput community sequencing data. Nat. Methods 7, 335–336 (2010).
Article CAS Google Scholar
Avershina, E., Frisli, T. & Rudi, K. De novo semi-alignment of 16S rRNA gene sequences for deep phylogenetic characterization of next generation sequencing data. Microbes Environ. 28, 211–216 (2013).
Article Google Scholar
Erb-Downward, J. R. et al. Use of direct gradient analysis to uncover biological hypotheses in 16S survey data and beyond. Sci. Rep. 2, 1–13 (2012).
Article Google Scholar
Lee, T. A., Rollwagen-Bollens, G., Bollens, S. M. & Faber-Hammond, J. J. Environmental influence on cyanobacteria abundance and microcystin toxin production in a shallow temperate lake. Ecotoxicol. Environ. Saf. 114, 318–325 (2015).
Article CAS Google Scholar
Lozupone, C. & Knight, R. UniFrac: a new phylogenetic method for comparing microbial communities. Appl. Environ. Microbiol. 71, 8228–8235 (2005).
Article CAS Google Scholar
Lozupone, C., Lladser, M. E., Knights, D., Stombaugh, J. & Knight, R. UniFrac: an effective distance metric for microbial community comparison. ISME J. 5, 169–172 (2011).
Article Google Scholar
Wei, J. X. et al. Graphene-reinforced titanium enhances soft tissue seal. Front. Bioeng. Biotechnol. 9, 665305 (2021).
Article Google Scholar
Koo, H. et al. Microbial communities and their predicted metabolic functions in growth laminae of a unique large conical mat from Lake Untersee, East Antarctica. Front. Microb. 8, 1347 (2017).
Article Google Scholar
Chang, F., He, S. S. & Dang, C. Y. Assisted selection of biomarkers by linear discriminant analysis effect size (LEfSe) in microbiome data. J. Vis. Exp. 183, e61715 (2022).
Google Scholar
Download references
The authors wish to acknowledge the financial support of the work was support of National Key Research and Development Plan of China (No. 2022YFB2603000), Key R&D Program of Shandong Province, China (No. 2022CXPT027), and MIITC High-tech Ship Research Projects (No. MC-202003-Z01-02).
Key Laboratory of Marine Environmental Corrosion and Bio-fouling, Institute of Oceanology, Chinese Academy of Science, Qingdao, 266071, China
Zhengquan Wang, Xiutong Wang, Yanliang Huang & Baorong Hou
University of Chinese Academy of Sciences, Beijing, 100049, China
Zhengquan Wang, Xiutong Wang & Yanliang Huang
Center for Ocean Mega-Science, Chinese Academy of Sciences, Qingdao, 266071, China
Zhengquan Wang, Xiutong Wang & Yanliang Huang
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
Z.W. drafted the paper and conducted the experimental work under the supervision of X.W. All authors evaluated and visualized the results. X.W. and Y.H. reviewed and edited the paper.
Correspondence to Xiutong Wang.
The authors declare no competing interests.
Publisher's note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
Reprints and Permissions
Wang, Z., Wang, X., Huang, Y. et al. Metagenomic insights into nutrient and hypoxic microbial communities at the macrofouling/steel interface leading to severe MIC. npj Mater Degrad 7, 41 (2023). https://doi.org/10.1038/s41529-023-00365-2
Download citation
Received: 19 January 2023
Accepted: 12 May 2023
Published: 24 May 2023
DOI: https://doi.org/10.1038/s41529-023-00365-2
Anyone you share the following link with will be able to read this content:
Sorry, a shareable link is not currently available for this article.
Provided by the Springer Nature SharedIt content-sharing initiative